Temanyl MS Primer - Vinyl primer
 
DESCRIPTION A one-component modified vinyl primer.
PRODUCT FEATURES Suitable for underwater steel, zinc and aluminium structures like ship bottoms etc. Used also as a primer under conventional and selfpolishing antifoulings. Can also be applied at low temperature conditions. Suitable to be used as a primer under vinyl, chlorinated rubber and acrylic topcoats.
Recommended uses Steel surfaces.
TECHNICAL DATA
Features Good abrasion, immersion and atmospheric resistance.
Colour Range Aluminium (reddish aluminium with Temaspeed tinting).
Gloss groups Matt
Coverage

Recommended film thicknesses

Theoretical coverage

dry

wet

 

60 µm

160 µm

6.3 m2/l

100 µm

265 µm

3.8 m2/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Thinner 1006
Application method By spray or brush.
Drying times

DFT 80 µm

+ 5 ºC

+ 10 ºC

+ 23 ºC

+ 35 ºC

Dust dry, after

2 h

1½ h

1 h

½ h

Recoatable, after

6 h

4 h

3 h

2 h

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Solids volume 38 ± 2 % volume (ISO 3233)
53 ± 2 % weight
Density 1.1 kg / l
Product code 008 6740
APPLICATION DETAILS
Application conditions The surface has to be dry. The temperature of the ambient air, surface or paint should not fall below - 5 ºC during application and drying. During application and drying the relative humidity should not exceed 80 %. The surface temperature should remain at least 3 ºC above the dew point.
Preparation Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)

Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Zinc surfaces: Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN ZN detergent.

Aluminium surfaces: Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873) If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with FONTECLEAN AL detergent.

Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Installation TEMANYL MS PRIMER, TEMABOND, TEMAZINC 77, TEMAZINC 88 and TEMAZINC 99.
Installation TEMACRYL AR 50 and TEMACHLOR 40.
Installation By spray or brush. Mix the paint thoroughly before use. Depending on the application method the paint can be thinned 0 - 5 %. Airless spray nozzle tip 0.018" - 0.023", spray angle 65º - 80º and nozzle pressure 15 MPa (150 bar).
Mixing of components Thinner 1006.
Cleaning of tools Thinner 1006
EU VOC 2004/42/EC-limit value The Volatile Organic Compounds amount is 540 g/litre of paint.
VOC content of the paint (thinned 5 % by volume) is 557 g/l.